Aluminium T profile, manufactured in alloy 6060 T66.
Supplied in lengths of 6,000 mm and in a raw finish.
On request and for minimum quantities, they can be supplied cut to size or in lacquered or anodised finishes.
Aluminium T profile, manufactured in alloy 6060 T66.
Supplied in lengths of 6,000 mm and in a raw finish.
On request and for minimum quantities, they can be supplied cut to size or in lacquered or anodised finishes.
| Total perimeter | Ixc | Iyc | Wxc | Wyc |
|---|---|---|---|---|
| 120 mm | 0.348 cm4 | 1.068 cm4 | 0.219 cm3 | 0.534 cm3 |
Aluminium T profile 40x20x2 is made from EN AW 6060 alloy. This is an aluminium alloy belonging to the 6000 family, with magnesium and silicon as the main alloying elements.
This aluminium alloy is particularly suitable for the manufacture of extruded profiles and offers an ideal balance between mechanical strength, corrosion resistance and suitability for decorative anodising.
Its extrusion capacity allows the manufacture of profiles with complex and functional designs regardless of their size. This feature, combined with its excellent finish through the anodising process, makes it ideal for all types of decorative elements or visible surfaces with aesthetic requirements.
This aluminium alloy has the following composition under standard EN 573-3:
|
|
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Ni |
Zn |
Ti |
Ga |
V |
Others |
Al |
|
|
Indiv. |
Total |
|||||||||||||
|
Min |
0.30 |
0.10 |
|
|
0.35 |
|
|
|
|
|
|
|
|
|
|
max. |
0.60 |
0.30 |
0.10 |
0.10 |
0.60 |
0.05 |
– |
0.15 |
0.10 |
– |
– |
0.05 |
0.15 |
Rest |
This aluminium profile, manufactured in EN AW 6060 alloy, has undergone T66 heat treatment to enhance its mechanical properties, achieving a balance between strength, elongation and suitability for anodising.
Its mechanical properties, in accordance with standard EN 755-2, are as follows:
|
Temper |
Profile thickness mm |
Rm MPa |
Rp0.2 MPa |
A min. |
A50 mm min. |
HBW hardness* |
||
|
min. |
Max. |
min. |
Max. |
|||||
|
T66 |
≤ 5 |
215 |
– |
160 |
– |
8 |
6 |
75 |
|
5 < e ≤ 25 |
195 |
– |
150 |
– |
8 |
6 |
75 |
|
*Reference value for information purposes only.
Upon request and minimum quantity, it is possible to supply the profile in other treatment states, such as T4, which may improve its bending capacity.
The EN AW 6060 alloy has the following physical properties:
|
Elastic modulus |
Coefficient of expansion per ºC (20º-100ºC) |
Thermal conductivity |
Resistivity µW·cm(2) /cm |
|
|
W/mK |
Cal/cm·s·°C |
|||
|
|
|
|||
|
69,000 MPa |
23.2 x 10-6 |
201 |
0.48 |
3.3 (T5) |
The general behaviour of the EN AW 6060 aluminium alloy is as follows in the areas listed below:
– Corrosion resistance: Very good.
– Weldability: Good.
– Formability: Good.
– Suitability for anodising: Excellent.
– Machinability: Good.
The classification is made in the following range: excellent, very good, good, fair and poor.
The main applications of the EN AW 6060 alloy are as follows:
– Construction and architecture: all types of profiles for carpentry, cladding, decorative and/or functional profiles, mouldings, trims, joints, etc.
– Standardised profiles with multiple applications in all types of structures.
– Special profiles designed for specific applications in all types of sectors: heat sinks, frames, moving parts, casings, protective covers, etc.
– Elements with high aesthetic requirements that must have an anodised finish.