Aluminium T profile, manufactured in alloy 6082 T6.
Supplied in lengths of 6,000 mm and in a raw finish.
On request and for minimum quantities, they can be supplied cut to size or in lacquered or anodised finishes.
Aluminium T profile, manufactured in alloy 6082 T6.
Supplied in lengths of 6,000 mm and in a raw finish.
On request and for minimum quantities, they can be supplied cut to size or in lacquered or anodised finishes.
| Total perimeter | Ixc | Iyc | Wxc | Wyc |
|---|---|---|---|---|
| 368 mm | 61.955 cm4 | 56.376 cm4 | 10.262 cm3 | 10.842 cm3 |
Aluminium T profile 104x80x6 is made of EN AW 6082 alloy. An aluminium alloy belonging to the 6000 family, with magnesium and silicon as the main alloying elements.
This aluminium alloy is particularly suitable for the manufacture of extruded profiles that require high strength and have a medium-complexity design. Among the commercial alloys commonly used in extruded profiles, it has the best mechanical characteristics, equivalent to the EN AW 6061 alloy commonly used in the American market.
Its extrusion capacity allows the manufacture of profiles with medium complexity and functional designs with high strength. It also has high corrosion resistance.
This aluminium alloy has the following composition under standard EN 573-3:
|
|
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Ni |
Zn |
Ti |
Ga |
V |
Others |
Al |
|
|
Indiv. |
Total |
|||||||||||||
|
min |
0.70 |
|
|
0.40 |
0.60 |
|
|
|
|
|
|
|
|
|
|
max. |
1.30 |
0.50 |
0.10 |
1.00 |
1.20 |
0.25 |
– |
0.20 |
0.10 |
– |
– |
0.05 |
0.15 |
Rest |
This aluminium profile, manufactured from EN AW 6082 alloy, has undergone T6 heat treatment to enhance its mechanical properties, achieving a balance between strength, elongation and suitability for anodising.
Its mechanical properties, in accordance with standard EN 755-2, are as follows:
|
Temper |
Profile thickness mm |
Rm MPa |
Rp0.2 MPa |
A min. |
A50 mm min. |
HBW hardness* |
||
|
min. |
Max. |
min. |
Max. |
|||||
|
T6 |
≤ 5 |
290 |
– |
250 |
– |
8 |
6 |
95 |
|
5 < e ≤ 25 |
310 |
– |
260 |
– |
10 |
8 |
95 |
|
*Reference value for information purposes only.
Upon request and minimum quantity, it is possible to supply the profile in other treatment states, such as T4, which may improve its bending capacity.
The EN AW 6082 alloy has the following physical properties:
|
Elastic modulus |
Coefficient of expansion per ºC (20º-100ºC) |
Thermal conductivity |
Resistivity µW·cm(2) /cm |
|
|
W/mK |
Cal/cm·s·°C |
|||
|
68,600 MPa |
23 x 10-6 |
185 |
0.44 |
3.8 |
The general performance of the EN AW 6082 aluminium alloy is as follows in the areas listed below:
– Corrosion resistance: Very good.
– Weldability: Good.
– Formability: Good.
– Suitability for anodising: Good.
– Machinability: Good.
The classification is made in the following range: excellent, very good, good, fair and poor.
The main applications of the EN AW 6082 alloy are as follows:
– Structural profiles for the naval sector, road and rail transport, and other types of applications with special strength requirements.